前言：PBT巴斯夫B 4520迅速冷却PBT
PBT巴斯夫B 4520迅速冷却PBT---Ultradur ? PBT B 4520>PBT<Notch impact: 3.75 kJ / M ?
Thermal deformation temperature: 162.77 ° C
Processing method: injection molding
Material properties: Injection grade
Material properties: Rapid cooling ? laser welding
Material usage: Office equipment application ? coil framework ? household appliance parts ? shell ? sewing machine ? commercial equipment
Vehicle specification: CHRYSLER MS-DB-400 CPN3942 Color:Non-matched Color ?
Ultradur? PBT B 4520>PBT<缺口冲击: 3.75 kJ/m?
热变形温度: 162.77 °C
加工方式: 注射成型
材料属性: 注塑级
材料特性: 迅速冷却 ? 激光焊接
材料用途: 办公室设备应用 ? 线圈骨架 ? 家电部件 ? 外壳 ? 缝纫机 ? 商业设备
汽车规格: CHRYSLER MS-DB-400 CPN3942 Color:Non-matched Color ?
| 比重 | 1.30 | g/cm? | ASTM D792, ISO 1183 |
| 溶化体积流率（MVR） (250°C/2.16 kg) | 19.0 | cm?/10min | ISO 1133 |
| 收缩率 - 流动 (3.18 mm) | 1.5 | % | |
| 吸水率 | |||
| 饱和 | 0.50 | % | ASTM D570 |
| 饱和, 23°C | 0.50 | % | ISO 62 |
| 平衡, 50% RH | 0.25 | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 130.0 | ml/g | ISO 1628 |
| 干燥温度 | 100 到 120 | °C | |
| 干燥时间 | 4.0 | hr | |
| 建议的 大水分含量 | 0.040 | % | |
| 加工（熔体）温度 | 250 到 270 | °C | |
| 模具温度 | 40.0 到 80.0 | °C | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 |