前言：ARLEN耐高温PA6T C230
ARLEN耐高温PA6T C230--ARLEN? PA6T C230>PA6T-GF30<
阻燃等级: HB
缺口冲击: 8.16 kJ/m?
熔融温度: 310 °C
符合规定:UL
材料用途:电子电器应用
三井化学
出光
ARLEN? PA6T C230N
>PA6T-GF30-FR<
阻燃等级: HB ? V-0
缺口冲击: 7.14 kJ/m?
熔融温度: 310 °C
符合规定:UL
材料用途:电子电器应用
PA6T C230物性信息：
| 密度 | 1.42 g/cc | 0.0513 lb/in? | ASTM D792 |
| 填料含量 | 30 % | 30 % | |
| Water Absorption | 0.3 % @Thickness 2.00 mm | 0.3 % @Thickness 0.0787 in | 24 hours in 23°C water; ASTM D570 |
| 3.0 % @Thickness 2.00 mm | 3.0 % @Thickness 0.0787 in | 24 hours in 100°C water; ASTM D570 | |
| 线性成型收缩率,Flow | 0.0050 cm/cm @Thickness 2.00 mm | 0.0050 in/in @Thickness 0.0787 in | ASTM D955 |
| 线性成型收缩率，横向 | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | Vertical Direction; ASTM D955 |