前言：超高韧性HDPE 9003台塑HDPE
超高韧性HDPE 9003台塑HDPE详情---The main features of taisox 9003 are: Chemical resistance
High resistance to environmental stress fracture (ESCR)
Good toughness
Typical application areas include:
Consumer goods
bottle
container
Medical / health care
HDPE 9003物性信息：
| 特性 | 超高韧性 高 ESCR（抗应力开裂） 高密度 耐化学性良好 耐洗涤剂 耐油性能 |
| 用途 | 工具/零件箱 化妆品 瓶子 玩具 药物 |
| 形式 | 粒子 |
| 加工方法 | 吹塑成型 |
| 密度 | 0.952 | g/cm? | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| 抗环境应力开裂 | 200 | hr | ASTM D1693 |
| 肖氏硬度 (邵氏 D) | 66 | ASTM D2240 |
| 抗张强度 | ASTM D638 | ||
| 屈服 | 27.9 | MPa | ASTM D638 |
| 断裂 | 34.3 | MPa | ASTM D638 |
| 伸长率 (断裂) | 1000 | % | ASTM D638 |
| 拉伸冲击强度 | 392 | kJ/m? | ASTM D1822 |
| 脆化温度 | -70.0 | °C | ASTM D746 |
| 维卡软化温度 | 124 | °C | ASTM D1525 |
| 熔融温度 | 132 | °C |