前言：PA6 BKV 115,朗盛 PA
PA6 BKV 115 朗盛 PA--CoPA，注塑级，15%玻璃纤维，弹性体改性，可电镀，在双轴冲击载荷下比BKV15具有更高的缺口冲击强度和更高的能量吸收，即使在干燥状态下，在单一情况下也可能不需要调节
CoPA, injection molding grade, 15% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 15, even in the dry state, conditioning may be unnecessary in single cases
Durethan? PA6 BKV 115 000000
>PA6-I-GF15<
ul
阻燃等级: HB
熔融指数: 29 g/10min
缺口冲击: 10 kJ/m?
热变形温度: 205 °C
物性信息：
| 密度 | 1.23 g/cc | 0.0444 lb/in? | ISO 1183 |
| 吸水率 | 8.5 % | 8.5 % | Test Sim. to ISO 62 |
| 平衡吸湿 | 2.5 % | 2.5 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| 粘度测试 | 134 cm?/g | 134 cm?/g | Viscosity number; ISO 307, 1157, 1628 |
| 线性成型收缩率,Flow | 0.0038 cm/cm | 0.0038 in/in | ISO 294-4, 2577 |